Stainless steel fiber products
Stainless steel fiber fabric
Item No.: WSW
Thickness: 0.5mm, 0.65mm, 0.68mm, 0.75mm
Weight: 580gsm, 650gsm, 800gsm, 980gsm
Width: 1m, 1.2m, 1.5m, 1.6m
Weave: twill
100% SUS 316L stainless steel fiber
Temperature service up to 1380deg C
Weight: 580gsm, 650gsm, 800gsm, 980gsm
Width: 1m, 1.2m, 1.5m, 1.6m
Weave: twill
100% SUS 316L stainless steel fiber
Temperature service up to 1380deg C
Description
- Woven from 100% S316L stainless steel fiber ( not stainless steel wire)
- Combine heat resistance and mechanical durability with the softness of a textile fabric.
- Smooth surface
- Used as mold separator and formed cushioning material for the automotive glass, glass bottles and CRT (TV) glass
- Improve the smooth appearance of glassl Used at 1200°F / 648°C continuously, Molten at 2500°F / 1371 °C
Other application required high temperature resistant together with friction resistant and electric conductivity.
1200°F / 648°C continuous rating, excellent mold separator and formed cushioning material for the automotive glass
Specification
| 1200°F / 648°C: Stainless Steel Fiber Woven Fabric | ||||||
| Part number | WKW580 | WKW650 | WKW800 | WKW980 | ||
| Material | SUS 316L | |||||
| Weave | Twill | |||||
| Filament diameter(μm) | 8 | 8 | 8, 12 | 8, 12 | ||
| Yarn count(Nm) | 16 Nm /2 | 12 Nm /2 | 8.6 Nm /2 | 6 Nm /2 | ||
| Thickness (mm) | 0.5±0.05mm | 0.65±0.05mm | 0.68±0.05mm | 0.75±0.05mm | ||
| Width (cm) | 100, 120, 150, 160 (±2%) | |||||
| Length(m) | 10 | |||||
| Weight (g/m2) | 580 (±3%) | 650 (±3%) | 800 (±3%) | 980 (±3%) | ||
| Ventilation Property(mm/s) | 1200(±8%) | 1180 (±3%) | 1100 (±3%) | 950 (±3%) | ||
| Melting Point | 1380℃ | |||||
| Thermal Resistant | 648℃ | |||||
| Chemical Composition of Raw Materials (%) | |||||||||
| SUS 316L | C | Si | Mn | Ni | Cr | Mo | N | S | P |
| 0.02 | 0.60 | 0.82 | 11.1 | 16.9 | 2.04 | 0.03 | 0.0005 | 0.027 | |